Analysis of the adhesive interface of dentine treated with carbodiimide and chitosan before cementation of fiberglass posts with different resin cements.

The objective of this study is to evaluate the effect of 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide (EDC) and chitosan (CHI) on the adhesive interface of resin cements to root dentine. Forty-five upper canines were sectioned, endodontically treated, prepared and divided into three groups according to dentine treatment (distilled water-DW, CHI 0.2% and EDC 0.5) and in three subgroups according to resin cement: RelyX ARC, Panavia F 2.0 or RelyX U200. Slices were obtained, with five slices of each third submitted to the analysis of the adaptation of the adhesive interface through scores and the perimeter with gaps in confocal laser scanning microscopy and one slice of each third later evaluated qualitatively in scanning electron microscopy. The results were analyzed using with Kruskal-Wallis and Spearman correlation tests. There was no difference in adaptation for the different resin cements (p = .438). EDC presented better adaptation when compared to the groups treated with DW and CHI (p < .001), while the CHI and DW presented similar adaptation values (p = .365). No difference was observed in the perimeter referring to the gap areas for the different resin cements (p = .510). EDC showed a lower percentage of perimeters with gaps when compared to CHI (p < .001), with the percentage of perimeter with gaps of teeth treated with CHI being lower than DW (p < .001). A positive correlation coefficient equal to 0.763 was obtained between the perimeter with gaps and the adaptation data of the adhesive interface (p < .001). EDC resulted in better adaptation of the adhesive interface and a lower percentage of perimeters with gaps compared to chitosan.

Effect of Carbodiimide (EDC) on the Bond Strength Longevity of Epoxy Resin-based Endodontic Sealer to Root Dentin: An In-Vitro Study.

PURPOSE: EDC (1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride) can increase dentin bonding longevity. This study aimed to evaluate the effect of final irrigation of the root canal with EDC on the bond strength (BS) longevity of an epoxy resin-based root-canal sealer. MATERIALS AND METHODS: Twenty maxillary canines were sectioned and standardized for root length at 17 mm. Roots were instrumented and distributed into 2 groups according to the final irrigation protocol: EDTA 17%+NaOCl 2.5% (C) and EDTA 17%+NaOCl 2.5%+EDC 0.5M (EDC). The canals were dried and filled with AH Plus (Dentsply Sirona). Three slices were obtained per third, and the first slice from each third was used for the immediate push-out test (i) followed by analysis of the failure pattern (n = 10); the second slice from each third was used for the push-out test after 6-month aging (A) followed by analysis of the failure pattern (n = 10); the third slice from each third was used to examine the adhesive interface under confocal laser scanning microscopy (CLSM) (n = 10). Data were analyzed with ANOVA, Fisher's exact and Kruskal-Wallis tests. RESULTS: Higher BSs were found for EDC-A (5.6 ± 1.9) than for EDC-I (3.3 ± 0.7), C-i (2.5 ± 1.0) and C-i (2.6 ± 1.0) (p = 0.0001), while C-A values were in some cases similar to C-i and in others similar to EDC-i. No statistically significant difference was observed between the thirds (p > 0.05), except for EDC-i, which showed lower BS for the cervical (2.79 ± 0.46) compared to the apical third (3.8 ± 0.5), while the middle third in some cases had values similar to those of the apical and in others to the cervical third (3.2 ± 0.7) (p = 0.032). More mixed adhesive failures were found in the cervical third, and more adhesive failures to the sealer occurred in the middle and apical thirds (p = 0.014). A significant difference was observed between treatments in terms of adaptation of the adhesive interface, with a higher percentage of good adaptation using EDC (66.7%) than using C (40%), and a lower percentage of poor adaptation with EDC (10%) compared to C (20%) (p < 0.05). CONCLUSION: Root canal irrigation with EDC increased the longevity of the adhesive interface of an epoxy resin-based root-canal sealer.

The impact of provisional intraradicular retainers cementation with temporary methacrylate-based resin in the bond strength of glass fiber posts to root dentin.

Chemical composition of temporary cements interferes in the bond strength and quality of the bond interface of glass fiber posts to root dentin. The aim of the present study was to evaluate the influence of different temporary cements on the bond strength of fiberglass posts and resin cement. Thirty-two maxillary central incisor roots were standardized at 15 mm length. The root canals were prepared with Reciproc R50 and filled with a R50 single cone and AH Plus. Ten mm of filling material was removed with a heated Schilder condenser, leaving 5 mm of apical filling material. The roots were randomly distributed into 4 groups (n = 8). In the control group, the root canal was prepared with a standard drill according to the post diameter (DC #1, FGM, Joinville, Brazil), irrigated with 5 mL of distilled water and immediately received the fiberglass post cemented with self-adhesive resin cement. For the other groups, cores were made with temporary intraradicular retainers cemented with different temporary cements: methacrylate-based resin (Bifix Temp - Voco), calcium hydroxide-based (Provicol - Voco) and zinc oxide-based - eugenol-free (Relyx Temp NE - 3M). After 7 days, mechanical removal of the temporary retainers, preparation, irrigation of the root canal and cementation of the fiberglass post were performed, following the same protocol that had been performed in the control group. The roots were sectioned to obtain 3 slices per root third. The most cervical section of each third was used for the push-out test and failure pattern analysis, while the most apical section was subjected to analysis of the adhesive interface by scanning electron microscopy (SEM). The BS data were compared between groups using the two-way ANOVA and Tukey post-test. The failure pattern results were expressed in percentage and compared between groups using the chi-square test and the material adaptation data at the bond interface were evaluated using the Kruskal-Wallis and Dwass-Steel-Critchlow-Fligner tests. The results showed higher BS in the cervical third, with a higher value in the control group (10.8 ± 0.94) and Bifix Temp group (9.78 ± 0.71), with no statistically significant difference between these groups (P > .05). The middle and apical thirds showed no statistically significant difference (P > .05). As regards the type of failure, a higher percentage of mixed adhesive failures was observed for all groups. Analysis of the adhesive interface by SEM showed that the temporary cement Bifix Temp showed greater adaptation at the bond interface. It was concluded that the methacrylate-based resin temporary cement showed the highest bond strength values and best adaptation to root dentin than the zinc oxide-based and calcium hydroxide-based temporary cements.